This Article Full Text (PDF) References Alert me when this article is cited Alert me if a correction is posted Citation Map Services Email this article to a friend Similar articles in this journal Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via HighWire Citing Articles via Google Scholar Citing Articles via Scopus Google Scholar Articles by Dusenbury, J.H. Articles by Wakelin, J.H. Search for Related Content Social Bookmarking                         What's this?

The Influence of Chemical Treatment on the Properties of Wool

I. Alkali Solubility as a Measure of Sulfuric Acid Degradation

Textile Research Institute, Princeton, New Jersey

E.H. Mercer

Textile Research Institute, Princeton, New Jersey

J.H. Wakelin

Textile Research Institute, Princeton, New Jersey

The view that the cortex of the wool fiber consists of a resistant fraction, the paracortex, and a less resistant fraction, the orthocortex, which extend in the form of two twisted hemi cylinders from one end of the fiber to the other, is used to explain the mechanism of the alkali- solubility test on acid-damaged wool. The effects of acid damage on several single-fiber prop erties and on the resistance of fabrics to flex abrasion have been measured for correlation with alkali-solubility data.

During the initial exposure of the wool to acid damage, alkali solubility is observed to in crease rapidly, corresponding to damage chiefly to the orthocortex; during the later stages, as the damage proceeds into the paracortex, the alkali solubility increases at a much slower rate with time of exposure. The decreases observed in the values for physical properties of the wool with increasing exposure to acid correspond generally with the changes in alkali solubility.

Wool treated with formaldehyde, either preceding or following a series of progressive expo sures to acid, exhibits greatly decreased alkali solubility, but fails to show a corresponding im provement in physical properties. It is suggested that the acid acts to degrade the wool fiber by hydrolyzing peptide bonds, and that the formaldehyde treatments decrease alkali solubility by a cross-linking mechanism that does little to improve the physical properties of the wool.

A good correlation was found between the flex-abrasion resistance of the variously treated fabrics and the energy to break of the corresponding single fibers. The product of breaking stress and breaking extension, a fiber property related to energy to break, was also found to correlate well with the fabric flex-abrasion resistance.

Textile Research Journal, Vol. 24, No. 10, 890-899 (1954)
DOI: 10.1177/004051755402401003


CiteULike    Complore    Connotea    Del.icio.us    Digg    Reddit    Technorati    Twitter    What's this?

This article has been cited by other articles:

				E. H. Hinton JR A Survey and Critique of the Literature on Crosslinking Agents and Mechanisms as Related to Wool Keratin Textile Research Journal, April 1, 1974; 44(4): 233 - 292. [Abstract] [PDF]

				J. H. Dusenbury, C.-N. Wu, and C. J. Dansizer Mechanical Properties of Feather and Down Fibers: Part I: Measurements at 65% RH and 70{degrees} F Textile Research Journal, April 1, 1960; 30(4): 277 - 290. [Abstract] [PDF]

				J. H. Dusenbury and A. B. Coe Differential Dyeing as an Indicator of Bilateral Structure in Wool: New Findings Textile Research Journal, April 1, 1955; 25(4): 354 - 358. [PDF]